文化大學機構典藏 CCUR:Item 987654321/5934
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 47249/51115 (92%)
Visitors : 14508993      Online Users : 1358
RC Version 6.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: https://irlib.pccu.edu.tw/handle/987654321/5934


    Title: 以押出法製備聚丙烯/氧化鋁有機無機奈米複合材料之研究
    Research on the Organic/Inorganic Nanocomposities of Polypropylene/Alumina by Extrusion
    Authors: 林凱鴻
    Contributors: 材料科學與奈米科技研究所
    Keywords: 聚丙烯
    奈米氧化鋁
    表面改質
    高分子奈米複合材料
    Date: 2007
    Issue Date: 2010-07-05 10:30:54 (UTC+8)
    Abstract: 本論文之研究目的是以矽烷偶合劑(3-methacryloxy-propyl-
    trimethoxysilane, MPS)對親水性表面的奈米氧化鋁粉末(Alumina, Al2O3)行表面改質,藉由偶合劑的兩極性在親水性的氧化鋁表面產生鍵結,而親油性的另一端便可以不受界面性質的影響,用雙螺桿壓出機以混鍊的方式,將改質後的奈米級氧化鋁粉末成功地到導入聚丙烯(Polypropylene, PP)中,形成奈米高分子複合材料,並與未改質前氧化鋁/聚丙烯高分子複合材料做比較。
    研究結果顯示,藉由紅外線光譜分析(FT-IR)官能基鑑定,改質劑已成功地在無機氧化鋁表面產生鍵結;由X光繞射分析儀(XRD)證明導入氧化鋁粉末並不會改變PP的結晶型態;由掃描式電子顯微鏡(SEM)可看出表面改質對其分散性與結合力的差異;在熱性質方面,我們得知因為有機的偶合劑會先提早裂解,但會幫助降低裂解速率,提高最大裂解溫度;機械性質方面我們可以得知改質過後的奈米氧化鋁/PP複合材料比未改質的奈米氧化鋁/PP複合材料有更強大的抗拉模數;根據本實驗結果顯示出,本研究改質成功並且已達到奈米級分散。
    To enhance the interfacial interaction in alumina nanoparticles extruded polypropylene composites, an effective surface modification method was developed by grafting 3-methacryloxy-propyl-trimethoxy-
    silane (MPS) onto the particles. We compared modified alumina- polypropylene nanocomposites with alumina-polypropylene composites.
    Results of infrared spectroscopy demonstrated that the desired MPS have been covalently bonded to the surface of the alumina nanoparticles. It was found that filled alumina nanoparticles did not changed poly- propylene crystal structure by XRD. SEM images were shown that the modification influenced dispersal and bounding force of alumina nano- particles. In the thermal properties, MPS dissociated at first, decreased dissociation rate of nanocomposites, and increased dissociation temper-
    ature. We analyzed that modified alumina-polypropylene nanocomposites tensile modulus were stronger than alumina-polypropylene nanocom-
    posites tensile modulus in the mechanical properties. As a result, it was a successful experiment that modification of alumina nanoparticles and nanoparticles nanodispersal.
    Appears in Collections:[Department of Chemical & Materials Engineering] thesis

    Files in This Item:

    File SizeFormat
    0KbUnknown242View/Open


    All items in CCUR are protected by copyright, with all rights reserved.


    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback