Title:	改變撥水劑濃度與壓吸條件對中底用聚酯針軋不織布之撥水性研究 Water Resistance of Needle Punching Nonwovens for Insoles by Agent and Padding Process Parameter
Authors:	許雅茹林永浩邢文灝
Contributors:	紡工系
Keywords:	不織布中底布撥水加工上劑率 non-woven fabric insoles water repellent
Date:	2015-03
Issue Date:	2017-06-26 10:47:56 (UTC+8)
Abstract:	現今鞋材織物，需具適當之透氣與撥水性能。添加少量氟系撥水劑即具顯著的撥水效果，耐久性亦優於有機矽類，C_8 型的氟系撥水劑，以浸漬壓吸法進行撥水加工。親疏水測試之結果為接觸角介於118~130°，撥水評級介於3~4 級，且加工前後經虹吸測試證明布面濕潤長度由80mm下降到0mm，顯示加工後織物疏水性優良。而透氣度介於1~1.49m/s，與原樣差異不大表示加工後變異不大，但水洗20 次後，接觸角下降17°，撥水評級下降1 級。綜合以上結果，其中上劑率1.51%時可得到128°之接觸角，且可耐水洗20 次後撥水評級下降1 級，對鞋材已具有良好的耐用性，為適當的加工條件。 One of them is C6-based fluorochemical water-repellent, which conforms to environmental protection. In this research, low melting point polyester of needle punching nonwovens were finished by C6-based fluorochemical water-repellent. About hydrophobicity test, the contact angles were constantly between 118 and 130゜and the rating results of spray test were between 3 and 4 level. The wicking height of finished fabric was 0 cm. The result show finished have better hydrophobicity. Air permeability of fabric was between 1 and 1.49m/s. After the fabric washed for 20 times, the contact angles were dropping 7゜and spray test were dropping 1 level. Above-mentioned results, one of them is 1.51% take up rate was a better option.
Relation:	華岡紡織期刊； 22卷1期 (2015 / 03 / 01) ， P10 - 17
Appears in Collections:	[Department of Textile Engineering ] Journal of the Hwa Gang Textile

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	157	View/Open

View Licence

Loading...