题名:	以水熱法轉化纖維素為具有附加價值化學品之研究 Conversion of Cellulose into Value-Added Chemicals by Hydrothermal Method
作者:	王敬中賴榕樺林仁斌
贡献者:	化材系
关键词:	纖維素水熱法球磨法 5-羥甲基糠醛生質能 Cellulose Hydrothermal method Ball-milling 5-HMF Biomass energy
日期:	2013-03
上传时间:	2017-03-23 13:30:09 (UTC+8)
摘要:	研究以水熱法將纖維素轉化為具有附加價值之化學品（e.g.葡萄糖、5-羥甲基糠醛(5-HMF)），探討球磨前處理與水熱反應條件（180~240℃，22~24 bar）對纖維素轉化反應產物之產率的影響。研究結果顯示經過球磨處理72小時後，纖維素的結晶度由原先的72%減少為20%。經球磨處理72小時的纖維素在溫度220℃與壓力22 bar條件下反應1小時後的葡萄糖與5-HMF產率可分別由2.9、10.5%提昇至11.5、34.0%；然而隨著反應時間的增長，這兩者的產率皆隨之降低，反應時間至12小時後的葡萄糖與5-HMF產率已分別減少為0.3、4.4%，這顯示最初反應生成的葡萄糖與5-HMF已進一步轉化為其他副產物。本研究結果可作為纖維素水熱轉化製程開發之基礎資料。 In this work, the cellulose was converted into value-added chemicals (e.g. glucose, 5-hydroxymethylfurfural (5-HMF)) by the hydrothermal method. The effects of the ball-milling pretreatment and the hydrothermal reaction conditions (180~240℃, 22~24 bar) on the product yields of cellulose conversion were investigated. The results showed that the crystallinity index of raw cellulose (72%) was reduced to 20% after a 72 hr of ball-milling. For 1 hr of reaction time under the hydrothermal condition (220℃, 22 bar), the yields of glucose and 5-HMF of the 72 hr ball-milled cellulose were respectively promoted to 11.5% and 34.0% comparing to those (2.9% and 10.5%) for the raw cellulose. Nevertheless, the yields of both the glucose and 5-HMF were decreased with the prolonged reaction time and were found to 0.3% and 4.4% for the reaction time as long as 12 hr. This indicated that the initial glucose and 5-HMF products were further converted into other side products. These results could be the basic data for the further design of cellulose hydrothermal conversion process.
關聯:	臺灣鑛業； 65卷1期 (2013 / 03 / 01) ， P38 - 44