Strong amorphization of high-entropy AlBCrSiTi nitride film

文化大學機構典藏 CCUR > 理工學院 > 工學院 > 化學工程與材料工程學系暨碩士班 > 期刊論文 > Item 987654321/24288

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://irlib.pccu.edu.tw/handle/987654321/24288

题名:	Strong amorphization of high-entropy AlBCrSiTi nitride film
作者:	Tsai, CW (Tsai, Che-Wei) Lai, SW (Lai, Sih-Wei) Cheng, KH (Cheng, Keng-Hao) Tsai, MH (Tsai, Ming-Hung) Davison, A (Davison, Andrew) Tsau, CH (Tsau, Chun-Huei) Yeh, JW (Yeh, Jien-Wei)
贡献者:	Inst Mat Sci & Mfg
关键词:	High-entropy alloy Nitride film Amorphous structure
日期:	2012-01
上传时间:	2013-02-25 10:45:41 (UTC+8)
摘要:	Amorphous coatings, particular nitride systems, are of interest for numerous practical applications. Nevertheless, at present only a few amorphous nitride coating systems have been considered, the most notably being the (TM, Si)N system (transition metal (TM) = Ti, Zr, W, Mo). The present study provides an alternative approach for producing amorphous nitride films with high thermal stability up to 700 degrees C for 2 h. Films are deposited from an equimolar AlBCrSiTi target in various argon/nitrogen atmospheres at different substrate temperatures. It is found that above the nitrogen flow ratio (i.e. R-N = N-2/N-2 Ar) of 28.6% a near equal ratio between target elements and nitrogen is approached, thus indicating the coatings have the chemical formula of (AlBCrSiTi)N. The glancing-angle X-ray diffractometer and transmission electron microscope investigations indicate that the coatings, regardless of nitrogen concentration or deposition temperature (up to 500 degrees C), are amorphous. Thermal treatment shows that the amorphous structure of this (AlBCrSiTi)N coating is maintained up to 700 degrees C when annealing for 2 h in vacuum. At annealing temperatures of 800 degrees C and above, the amorphous films transform into a simple NaCl-type face-centered cubic solid solution. Even after annealing at 1000 degrees C for 2 h, the grain size is only 2 nm. High entropy effect, large lattice distortion effect, and sluggish diffusion effect are proposed to account for the formation of amorphous nitrides. Crown Copyright (C) 2011 Published by Elsevier B.V. All rights reserved.
關聯:	THIN SOLID FILMS 卷: 520 期: 7 頁數: 2613-2618
显示于类别:	[化學工程與材料工程學系暨碩士班] 期刊論文