| 題名: | Fracture behaviors of silane-cured metallocene-catalyzed polyethylene thermoplastic vulcanizate |
| 作者: | Lai, S.M.;Wu, T.H. |
| 貢獻者: | 材料科學與奈米科技研究所 |
| 日期: | 2005 |
| 上傳時間: | 2009-10-30 13:07:13 (UTC+8) |
| 摘要: | Silane moisture-cured metallocene-catalyzed polyethylene (mPE) blend to form a novel thermoplastic vulcanizate (TPV) has been prepared. Metallocene polyethylenes with two different levels of comonomer contents were grafted with various amounts of vinyltriethoxy silane. As a result, tensile strength varies slightly with increasing the levels of silane concentrations, at all test temperatures. Tear strength generally decreases with reduced energy dissipation, at higher degrees of cure. "Threshold" fracture energy is roughly proportional to the reciprocal square root of Young's modulus. By relating tensile strength to tear strength, it was found that the corrected average depth of flaw is in the range of 29.3 +/- 7.2 mu m, which successfully confirms the extension of Rivlin and Thomas's theory for conventional elastomers to TPVs under an elaborate treatment, due to the limitation of the theory. Cutting strength of mPE TPVs gives an intermediate value when compared with that of crystalline plastics and conventional elastomers, which further signifies the importance of crystalline yielding even in the nanofracture zone of deformation. (c) 2005 Wiley Periodicals, Inc. |
| 關聯: | JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS v.43 n.16 Pages: 2207-2218 |
| 顯示於類別: | [化學工程與材料工程學系暨碩士班] 期刊論文
|
文件中的檔案:
| 檔案 |
描述 |
大小 | 格式 | 瀏覽次數 |
|---|
| index.html | | 0Kb | Text | 1962 | 檢視/開啟 |
|
在CCUR中所有的資料項目都受到原著作權保護.
|