Title:	Fermentation, biodegradation and tensile strength of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) synthesized by Delftia acidovorans
Authors:	Hsieh, WC (Hsieh, Wen-Chuan) Wada, Y (Wada, Yuki) Chang, CP (Chang, Chih-Pong)
Contributors:	紡工系
Keywords:	COMAMONAS-ACIDOVORANS POLY(4-HYDROXYBUTYRIC ACID) HYDROGENOPHAGA-PSEUDOFLAVA MICROBIAL SYNTHESIS ESCHERICHIA-COLI BIOSYNTHESIS DEGRADATION SCAFFOLDS CELLS
Date:	2009-03
Issue Date:	2011-12-09 10:45:16 (UTC+8)
Abstract:	This study discusses poly(3-hydroxybutyrate-co-4-hydroxybutyrate) that is produced by Delftia acidovorans bacteria in fed-batch cultures from various carbon sources. The experimentally determined optimal fed-batch culture conditions are as follows: pH: 7.0, incubation temperature: 26 degrees C, incubation time: 72 h, and concentration of carbon source: 10 g/L. The maximum 4HB unit composition of P(3HB-co-4HB) obtained using the fed-batch culture with a cell concentration of about 2.5 g/L was 94 mol% although the P(3HB-co-4HB) content remained low, at around 13 wt%. The extent of the enzymatic degradation of P(3HB-co-4HB) was determined by involved PHB depolymerase and lipase. The tensile strength of P(3HB-co-4HB) markedly decreased during 2 h of degradation by PHB depolymerase, whereas that of P(3HB-co-4HB) degraded by lipase for 50 h was at least 3 MPa. (C) 2008 Taiwan Institute of Chemical Engineers. Published by Elsevier B.V. All rights reserved.